Phase Retardation Reflector Silicon
.750ӯ X .120 E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
1.00ӯ X .120 E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
1.10”Ø X .120” E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
1.50”Ø X .160” E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
2.00”Ø X .200” E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
2.00ӯ X .375" E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average @ 10.6µm for 45° AOI operation
Phase Retardation Reflector Silicon
3.00”Ø X .250” E.T.
Phase Shift: 90° ±3.0°
Coated: PRR Type
Reflectance > 99.0% average
@ 10.6µm for 45° AOI operation
Turning Mirrors Silicon DBMR
.500"Ø X .120" E.T.
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
.500"Ø X .120" (3.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon DBMR
.750"Ø X .120" E.T.
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
.750"Ø X .120" (3.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon DBMR
1.00"Ø X .120" Thick
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
1.00"Ø X .120" (3.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon DBMR
1.10"Ø X .120" E.T.
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
1.10"Ø X .120" (3.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon DBMR
1.50"Ø X .160" E.T.
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
1.50"Ø X .160" (4.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon DBMR
2.00"Ø X .200" E.T.
Coated: Reflectance > 99.7% average @ 10.6 µm
Reflectance: > 85% average for .633 µm and .650 µm 45° AOI
Absorption: < .30% @ 10.6 µm
Turning Mirrors Silicon EM
2.00"Ø X .200" (5.0mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Turning Mirrors Silicon EM
3.00"Ø X .250" (6.35mm) E.T.
Coating: Enhanced Metal Type
Reflectance > 99.6% average reflectance @10.6µm
Optimized for 45° AoI operation
Zero Phase Reflectors-Silicon
.500"Ø X .120" E.T. Coating:
Zero Phase Shift Type
Phase Shift: 0° ±2.0°
Reflectance > 99.6% @ 10.6µm
for 45° AOI operation
Zero Phase Reflectors-Silicon
.750"Ø X .120" E.T.
Coating: Zero Phase Shift
Type Phase Shift: 0° ±2.0°
Reflectance > 99.6% @ 10.6µm
@45º Angle of Incidence operation
Zero Phase Reflectors-Silicon
1.00"Ø X .120" E.T.
Coating: Zero Phase Shift
Type Phase Shift: 0° ±2.0°
Reflectance > 99.6% @ 10.6µm
@45º Angle of Incidence operation
Zero Phase Reflectors-Silicon
1.10"Ø X .120" E.T. Coating:
Zero Phase Shift Type
Phase Shift: 0° ±2.0°
Reflectance > 99.6% @ 10.6µm
for 45° AOI operation